HDPE is a high degree of crystallinity Nonpolar thermoplastic resin,and HDPE Geomembrane is a kind of geosynthetic materials, it is a (middle), high density polyethylene resins as raw material to produce a waterproof barrier materials.

It has excellent resistance to environmental stress cracking resistance, low temperature resistance, aging resistance, corrosion resistance, as well as large temperature range ( -60–60) and a long service life (50) and Widely used in solid waste landfill seepage, solid waste treatment and landfill seepage, seepage of sewage treatment plant, an artificial lake seepage, seepage from tailings.

show

 

 

 

 

 

 

 

 

 

show1

 

 

 

 

 

 

 

 

show2

 

 

 

 

 

 

 

 

Specification

No. Item               Test Value
0.75mm 1.0 mm 1.25 mm 1.5 mm 2.0 mm 2.5 mm 3.0mm
1 Minimum Density(g/cm³) 0.939
2 Tensile Property
Strength at yield,N/mm 11 15 18 22 29 37 44
Strength at break ,N/mm 20 27 33 40 53 67 80
Elongation at yield,% 12
Elongation at break,% 700
3 Tear Resistance   N 93 125 156 187 249 311 374
4 Puncture Resistance  N 240 320 400 480 640 800 960
5 Stress Crack Resistance, hrs 300
 6 Carbon Black Content, % 2.0-3.0
Carbon Black Dispersion 1  or  2
 7 Standard OTI  Min 100
High Pressure OTI  Min 400
8 Impact Cold Crack at -70°C Pass
9 Water vapor permeability(g.cm/cm2 .s.Pa) ≤1.0×10-13
10 Dimensional Stability (%) ±2

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

HDPE Geomembrane -Smooth GRI GM13 Standard
Properties Test Method Test Value
0.75mm 1.00 mm 1.50 mm
Thickness – mils (min. ave.)·lowest individual of 10 values D5199 nom. (mil)-10% nom. (mil)-10% nom. (mil)-10%
Density (min.) D 1505/
D 792
0.940 g/cc 0.940 g/cc 0.940 g/cc
Tensile Properties (1) (min. ave.)·
yield strength·
break strength·
yield elongation·
break elongation
D 6693
Type IV
11 kN/m
20 kN/m
12%
700%
15 kN/m
27 kN/m
12%
700%
22 kN/m
40 kN/m
12%
700%
Tear Resistance  (min. ave.) D 1004 93N 125 N 187 N
Puncture Resistance (min. ave.) D 4833 240N 320 N 480 N
Stress Crack Resistance (2) D 5397(App.) 300 hr. 300 hr. 300 hr.
Carbon Black Content – % D 4218 (3) 2.0-3.0% 2.0-3.0% 2.0-3.0%
Carbon Black Dispersion D 5596 note (4) note (4) note (4)
Oxidative Induction Time (OIT)(min. ave.) (5)
(a) Standard OIT— or —
(b) High Pressure OIT
D 3895
D 5885
100 min.
400 min.
100 min.
400 min.
100 min.
400 min.
Oven Aging at 85°C (5), (6)
(a) Standard OIT (min. ave.)- % retained after 90 days— or —
(b) High Pressure OIT (min. ave.)- % retained after 90 days
D 5721
D 3895
D 5885
55%
80%
55%
80%
55%
80%
UV Resistance (7)
(a) Standard OIT (min. ave.)— or —
(b) High Pressure OIT (min. ave.)- % retained after 1600 hrs
D 3895
D 5885
N.R. (8)
50%
N.R. (8)
50%
N.R. (8)
50%

 

application zong

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

Why choose us

why choose us

 

 

 

 

 

 

 

 

 

 

Packing and shipping

packing shipping1

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

Factory

factory1

 

 

 

 

 

 

 

 

factory

 

Have any question, Please enter the form below and click the submit button.

*
*
1 + 6 = ?
Please enter the answer to the sum & Click Submit to verify your registration.
CATEGORY AND TAGS:

Geotextile

Related Items

  • Product Categories

  • Contact Us


    Questions?
    Deyang Sunrise International Co.,Ltd
    +86.13228613228

    manager@dysunrise.com
    Skype:yunchuan.xiao

    24 hours every day
    7 days every week